Composition dependence of electronic, magnetic, transport and morphological properties of mixed valence manganite thin films
Singh, Freeland, Fitzsimmons, Jeen, Biswas · cond-mat.str-el · 2015-09-28 · 原文
We present a comparison of the in-plane length scale over which charge and magnetism are correlated in (La0.4Pr0.6)1-xCaxMnO3 films with x = 0.33 and 0.375, across the metal to insulator transition (MIT) temperature. We combine electrical transport (resistance) measurements, x-ray absorption spectroscopy (XAS), x-ray magnetic circular dichroism (XMCD), and specular/off-specular x-ray resonant magnetic scattering (XRMS) measurements as a function of temperature to elucidate relationships between electronic, magnetic and morphological structure of the thin films. Using off-specular XRMS we obtained the charge-charge and charge-magnetic correlation length of these LPCMO films near the MIT. The charge-magnetic correlation length (~ 12000 Å) for x = 0.33 was much larger (~4 times) than the charge-charge correlation length (~ 3200 Å) at 20 K. Whereas for x = 0.375 the charge-magnetic correlation length (~ 7500 Å) was smaller than the charge-charge correlation length (~ 9000 Å).
讲义
讲义·推断 依据「原文」自动生成的结构化摘要（推断），非原文表述；以原文为准。
1. 人话版
We present a comparison of the in-plane length scale over which charge and magnetism are correlated in (La0.4Pr0.6)1-xCaxMnO3 films with x = 0.33 and 0.375, across the metal to insulator transition (MIT) temperature.
We combine electrical transport (resistance) measurements, x-ray absorption spectroscopy (XAS), x-ray magnetic circular dichroism (XMCD), and specular/off-specular x-ray resonant magnetic scattering (XRMS) measurements as a function of temperature to elucidate relationships between electronic, magnetic and morphological structure of the thin films.
2. 领域脉络
本文类目：cond-mat.str-el，属于其所在研究脉络的最新进展。
3. 机制拆解
Using off-specular XRMS we obtained the charge-charge and charge-magnetic correlation length of these LPCMO films near the MIT.
4. 证据与数字
The charge-magnetic correlation length (~ 12000 Å) for x = 0.33 was much larger (~4 times) than the charge-charge correlation length (~ 3200 Å) at 20 K.
Whereas for x = 0.375 the charge-magnetic correlation length (~ 7500 Å) was smaller than the charge-charge correlation length (~ 9000 Å).