Enhanced critical-current in P-doped BaFe2As2 thin films on metal substrates arising from poorly aligned grain boundaries
Sato, Hiramatsu, Kamiya, Hosono · cond-mat.supr-con · 2016-11-13 · 原文
Thin films of the iron-based superconductor BaFe2(As1-xPx)2 (Ba122:P) were fabricated on polycrystalline metal-tape substrates with two kinds of in-plane grain boundary alignments (well aligned (4 deg.) and poorly aligned (8 deg.)) by pulsed laser deposition. The poorly aligned substrate is not applicable to cuprate-coated conductors because the in-plane alignment >4 deg. results in exponential decay of the critical current density (Jc). The Ba122:P film exhibited higher Jc at 4 K when grown on the poorly aligned substrate than on the well-aligned substrate even though the crystallinity was poorer. It was revealed that the misorientation angles of the poorly aligned samples were less than 6 deg., which are less than the critical angle of an iron-based superconductor, cobalt-doped BaFe2As2 (~9 deg.), and the observed strong pinning in the Ba122:P is attributed to the high-density grain boundaries with the misorientation angles smaller than the critical angle. This result reveals a distinct advantage over cuprate-coated conductors because well-aligned metal-tape substrates are not necessary for practical applications of the iron-based superconductors.
讲义
讲义·推断 依据「原文」自动生成的结构化摘要（推断），非原文表述；以原文为准。
1. 人话版
Thin films of the iron-based superconductor BaFe2(As1-xPx)2 (Ba122:P) were fabricated on polycrystalline metal-tape substrates with two kinds of in-plane grain boundary alignments (well aligned (4 deg.) and poorly aligned (8 deg.)) by pulsed laser deposition.
The poorly aligned substrate is not applicable to cuprate-coated conductors because the in-plane alignment >4 deg.
2. 领域脉络
本文类目：cond-mat.supr-con，属于其所在研究脉络的最新进展。
3. 机制拆解
results in exponential decay of the critical current density (Jc).
4. 证据与数字
The Ba122:P film exhibited higher Jc at 4 K when grown on the poorly aligned substrate than on the well-aligned substrate even though the crystallinity was poorer.
It was revealed that the misorientation angles of the poorly aligned samples were less than 6 deg., which are less than the critical angle of an iron-based superconductor, cobalt-doped BaFe2As2 (~9 deg.), and the observed strong pinning in the Ba122:P is attributed to the high-density grain boundaries with the misorientation angles smaller than the critical angle.