The doping efficiency of lithium deposited at cryogenic temperatures on epitaxial and CVD monolayer graphene has been investigated under ultra-high vacuum conditions. Change of charge carrier density was monitored by gate voltage shift of the Dirac point and by Hall measurements, in low and high doping regimes. It was found that pre-annealing the graphene greatly enhanced the maximum levels of doping that could be achieved: doping saturated at Δn = 2\times 10^{13} e^-/cm^2 without annealing, independent of sample type or previous processing; after a 900 K anneal, the saturated doping rose one order of magnitude to Δn = 2\times 10^{14} e^-/cm^2.
讲义
讲义·推断 依据「原文」自动生成的结构化摘要（推断），非原文表述；以原文为准。
1. 人话版
The doping efficiency of lithium deposited at cryogenic temperatures on epitaxial and CVD monolayer graphene has been investigated under ultra-high vacuum conditions.
Change of charge carrier density was monitored by gate voltage shift of the Dirac point and by Hall measurements, in low and high doping regimes.
2. 领域脉络
本文类目：cond-mat.mes-hall，属于其所在研究脉络的最新进展。
3. 机制拆解
摘要未展开方法细节——精读时重点看方法/模型部分。
4. 证据与数字
It was found that pre-annealing the graphene greatly enhanced the maximum levels of doping that could be achieved: doping saturated at Δn = 2\times 10^{13} e^-/cm^2 without annealing, independent of sample type or previous processing; after a 900 K anneal, the saturated doping rose one order of magnitude to Δn = 2\times 10^{14} e^-/cm^2.
5. 反例与边界
摘要未声明局限与反例——这是需要警惕的信号，精读时先问边界。
6. 跨领域连接与意外收获
思考本文机制能否迁移到你正在跟进的问题。
7. 可复用方法
把本文机制与你手头项目对照，找一个两周内能验证的最小实验。
8. 术语表
精读时把不熟的术语记入此处，作为下次回忆的锚点。